XJ002 FLUX
SPECIFICATION£ºGB/T5293-1999 AWS A5.17-97 AWS A5.23-97
CLASSIFICATION£ºF4A4-H08MNA F6A4-EH12 F8A4-EA2-A2 F5A4-10MN2 F7A4-EH14
INTRODUCTION£ºXJ002 IS AN AGGLOMERATED FLUX OF THE BASIC TYPE£¬BASICITY INDEX IS 3.1£¬IT IS GREYWHIITE-SPHERICAL FLUX WITH GRAIN FROM 10 TO 60 MESHES£¬DENSITY IS 1.2-1.3 GRAM/CM3£¬WELDING CAN BE DONE ON AC AND DC+.
THE XJ002 FLUX BELONGS TO METAL LURGY NEUTRAL£¬A LITTLE SI AND MN IN THE WELD METAL INCREASE£¬BECAUSE MN LOSS OF WIRE£¬ISN¡¯T MORE,IT CAN BE MATCHED HIGH MN WIRES IN WELDING,IT CAN BE OBTAINED HIGH TOUGHNESS AT LOW TEMPERATURE,IT HAS SHORT SLAG CHARACTERS.
APPLICATION:XJ002 FLUX IS SUITABLE FOR WELDING X52,X60,X65,X70 PIPE STEELS AND IMPORTANT PRESSURE AND MATCHING MULTI-WIRE AND TANDEM-WIRE.
NOTE:BEFORE WELDING,BAKED 2HR FLUX OF 350¡æ AND REMOVED RUST,OIL,MOISTURE ECT OF PALATE.
MAIN COMPOUND(%)
SIO2+TIO2 |
CAO+MGO |
AL2O3+MNO |
CAF2 |
S |
P |
10-20 |
30-40 |
20-30 |
¡Ü30 |
¡Ü0.06 |
¡Ü0.08 |
MECHANICAL PROPERTY
MATCHING
WIRE |
TENSILE
STRENGTH£¨MPA£© |
YIELD
STRENGTH£¨MPA£© |
TEMPERATURE |
CHARPY-VOTCH
IMPACT
WORK£¨J£© |
H08MNA |
450-550 |
360-460 |
-40¡æ |
¡Ý34 |
H10MN2A |
500-600 |
400-500 |
-40¡æ |
¡Ý34 |
H08C(A) |
600-650 |
460-520 |
-40¡æ |
¡Ý34 |
|